310/310S/310H Stainless steel coil
Types 310 Stainless Steel and 310S are typically used for elevated temperature applications. Their high nickel and chromium contents impart excellent elevated temperature strength and resistance to oxidation compared to Type 304 SS. Type 310S Stainless Steel is identical to Type 310 except for a lower carbon content that minimizes carbide precipitation and improves weldability. They are essentially nonmagnetic as annealed and become lightly magnetic when cold worked.310 stainless steel flat rolled coil is primarily used for high-temperature situations.


Product Details

Product Name

Stainless Steel Strip Coils Grade 310/310S/310H

Coil weight

3-10 ton or as required

Width

3.5mm～1550mm or as required

Thickness

0.2mm～40mm or as required

Standard

ASTM,UNS,JIS,GB

Technique

Hot rolled / cold rolled

Surface Treatment

2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, chequered, embossed, hairline, sand blast, Brush, etching, Hot rolled plate (HR), Cold rolled sheet (CR), SATIN (Met with Plastic Coated) etc

Thickness Tolerance

±0.01mm~ ±0.25mm

Material

310/310S/310H stainless steel

Application

Petroleum, electronics, chemical industry, medicine, light textile, food, machinery, construction, nuclear power, aerospace, military industry and other industries.

MOQ

1 ton , We can accept sample order.

Shipment Time

Within 15-20 workdays after receiving deposit or workable L/C

Export Packing

Standard Export Seaworthy Package.Suit for all kinds of transport,or as required

Capacity

250,000 tons/year



Chemical Composition:

Weight % (all values are maximum unless a range is otherwise indicated)

Grade 310 310S 310H
C 0.25 0.08 0.40 min. - 0.10 max.
Si 1.5 1.5 0.75
Mn 2.0 2.0 2.0
Cr 24.0 min.-26.0 max. 24.0 min.-26.0 max. 24.0 min.-26.0 max.
Ni 19.0 min.-22.0 max. 19.0 min.-22.0 max. 19.0 min.-22.0 max.
P 0.045 0.045 0.045
S 0.03 0.03 0.03




Physical Properties :

Density Thermal Conductivity 212°F (100°C)
0.285 lbs/in3 8.0 BTU/hr/ft2/ft/°F
7.89 g/cm3 10.8 W/m-°K
Specific Heat Melting Range
0.12 BTU/lb-°F (32 – 212°F) 2470 – 2555°F
502 J/kg-°K (0 – 100°C) 1354 – 1402°C
Modulus of Elasticity Electrical Resistivity
28.5 x 106 psi 30.7 Microhm-in at 68°C
196 GPa 78.0 Microhm-cm at 20°C





Mechanical Properties:

Typical Values at 68°F (20°C)

Yield Strength Ultimate Tensile Elongation Hardness
0.2% Offset Strength in 2 in.
psi (min.) (MPa) psi (min.) (MPa) % (min.) (max.)
35,000 245 80,000 550 45 217 Brinell











FAQ:


Q1. What are your company's main products ?

A1: Our main products are stainless steel plate/sheet, coil, round/square pipe, bar, channel, etc.


Q2. How do you control quality ?

A2: Mill Test Certification is supplied with shipment, Third Party Inspection is available. and we also get ISO,SGS,Alibaba Verified.


Q3. What are the advantages of your company ?

A35: We have many professionals, technical personnel, more competitive prices and best after-dales service than other stainless steel companies.


Q4: What is the terms of packing?

A3: generally, we pack our goods in bundles or coils with rods or belts, we could also pack the goods as the customers requirement.


Q5:What is your delivery time?

A4: For stocks, we could transport the goods to loading port within 7 days after we received your deposit

For production period, it usually takes about 15 days-30 days after receiving the deposit.


Q6. Can you provide sample ?

A7: We can provide the samll samples in stock for free, as long as you contact us.

Customized samples will take about 5-7days.


Q7. How many coutries you already exported ?

A6: Exported to more than 50 countries mainly from America, Russia, UK, Kuwait, Egypt, Turkey, Jordan,India, Vietnam, Thailand, South Korea etc.




Contact us
Related Products
Return>>
Order Now!