Current Location : Home > Products > Stainless steel pipe > 904L stainless steel...
904L stainless steel pipe

904L is a highly alloyed, low carbon containing, non-stabilized austenitic stainless steel grade. Copper has been added to the alloy of 904L Stainless Steel Pipe. Hence, its resistance to strong reducing acids such as sulfuric acid is very high. The lower content of carbon makes it easier to produce the AISI 904L Welded Pipe according to specification ASTM A312. Though the content of carbon is lower, these pipes could be used for high temperature applications. The significant inclusion of nickel to the alloy of ASME SA 312 TP904L makes it possible for the pipes to have an outstanding performance even in elevated settings. Along with being a non-magnetic alloy, the Stainless Steel 904L Pipe also exhibits good resistance to stress related corrosion cracking. The presence of molybdenum in the alloy reduces the occurrence of crevice corrosion. Along with being used in applications between moderate to high temperatures, the ASTM A312 TP904L is primarily useful for general corrosion applications.


Product Details


Product name

Stainless Steel Pipe

Material

304,304L,321,316L,309S,310S,2205,2507,904L,926L,etc.

Outsider Diameter

6-1500mm 

Wall Thickness

0.5-120mm

Surface

2B, BA, 8K, No. 4, No.1  

Application

Building materials, kitchen ware, water heater, medical instrument...

Feature

corrosion resistance, heat resistance

Type

pipe

Size

standard size and other size as your requirement support



Chemical Composition:

Grade C Mn Si P S Cr Mo Ni Cu
904L min. - - - - - 19 4.0  23 1.0 
max. 0.02 2.0  1.0  0.045 0.035 23 5.0  28 2.0 




Mechanical Properties:

Grade Tensile Strength (MPa) min Yield Strength 0.2% Proof (MPa) min Elongation (% in 50mm) min Hardness
Rockwell B (HR B) Brinell (HB)
904L 490 220 36 70-90 typical 150






 